|Type:||Lead Acid Forklift Battery(without Electrolyte)||Voltage:||48v|
|Size:||Customized 570 X 980 X 780mm X 6mmt||Cycles:||1500 Times|
|Quantity Of Cells:||24||Material:||Lead, Plastics, Steel|
|Connection:||Screw/soft||Color Of Tray:||Red, Black, Grey|
|Plates:||Positive Tubular Plates||Watering System:||Optional|
1. Excellent battery charging performance, so that you can use it after loading, eliminating the trouble of adding acid for initial charging.
2. Sufficient battery capacity ensures good high current start-up and long-time deep discharge performance.
3. Advanced alloy formula and high-purity multicomponent lead based alloy make the grid have good corrosion resistance, small gas evolution, low water loss and small self discharge, so as to ensure the long service life of the battery.
|Type||Lead Acid 630AH 48v Traction Battery For Forklift 1500 Times cycles|
|Application||Electric Forklift Truck|
|Width of cell||158mm|
|Technology||Tubular Positive Plates|
|Cell Quantities||24 cells|
|Connection Type||Flexible/Soft connection|
|Steel Tray Size||Standard or Customized|
There are many reasons of the cells’ troubleshooting, except for the quantity and the storage, operating wrongly and unmerited maintenances are also one of the most important reasons.
If you find troubleshooting, analyze the reasons in time and take effective measures to eliminate it.
The features of the familiar troubleshooting and the reason and the methods of checking and repairing are as following:
1. Internal short-circuit
The charge voltage is always lower than normal; the discharge capacity is lower than normal; the discharge voltage quickly reduced to the final voltage; the voltage and the specific gravity raise slowly, and less or without gassing at the end of charge; the temperature of the electrolyte is high and raise faster during charge; the self-discharge is serious.
1.2 Probable causes
There are many reasons for short-circuit: conducting materials enter the cells connecting the positive and negative plates; the separator is damaged; the plates give birth to the lead bulb and store at the ear of the plates making short-circuit; the active materials are expanded or shed, the sediment touch the bottom of the plates leading short-circuit.
1.3 Possible remedy
First check if there are conducting materials entering the cells, if there are, remove the conductors. Remove the plates group checking if the lead-bulb expend leading short-circuit, if it is, remove the lead-bulb and change the electrolyte. If the separator is damaged, separate the plates group and find the damaged one and change a new one.
2. The reversible vitriolic salt of the plates
The discharge capacity is reduced and the specific gravity is lower than normal; during charge, the initial and the final voltage is higher than normal; the gassing appears too early and the temperature of the electrolyte raise fast and easy to exceed 55℃; voltage reduces too fast when discharge and reduces to the final voltage too early.
2.2 The reasons of troubleshooting
The cells are often weakly charged or not equalizing charged in time or often over-discharging or small-current discharging, in the station of half-discharging or discharging for a long time, or the level of the electrolyte is too low and some other reasons make the vitriolic lead in the positive and negative plates hard to transform into the active materials.
2.3 The ways to solve the problem
For the cells of plates with vitriolic salt, if it is not serious, you can revert by proper over-charging; for the serious ones, you can charge with small current; for the most serious ones, you can deal with them by using hydropath. In the sake of protection from it, you should operate according to the service manual and take equalizing charge in time.
Vent cap watering level